API 5L/A106/A53 choksiz po'lat quvur issiq haddelenmiş
|
Standart |
Baho |
Kimyoviy komponentlar (%) |
Mexanik xususiyatlar |
|||||
|
ASTM A53 |
C |
Si |
Mn |
P |
S |
Kuchlanish kuchi (Mpa) |
Hosildorlik kuchi (Mpa) |
|
|
A |
0 dan kichik yoki unga teng.25 |
- |
0 dan kichik yoki unga teng.95 |
0 dan kichik yoki unga teng.05 |
0 dan kichik yoki unga teng.06 |
330 dan katta yoki unga teng |
205 dan katta yoki teng |
|
|
B |
0 dan kichik yoki unga teng.30 |
- |
1,2 dan kam yoki teng |
0 dan kichik yoki unga teng.05 |
0 dan kichik yoki unga teng.06 |
415 dan katta yoki unga teng |
240 dan katta yoki teng |
|
|
ASTM A106 |
A |
0 dan kichik yoki unga teng.30 |
0 dan katta yoki unga teng.10 |
0.29-1.06 |
0 dan kichik yoki unga teng.035 |
0 dan kichik yoki unga teng.035 |
415 dan katta yoki unga teng |
240 dan katta yoki teng |
|
B |
0 dan kichik yoki unga teng.35 |
0 dan katta yoki unga teng.10 |
0.29-1.06 |
0 dan kichik yoki unga teng.035 |
0 dan kichik yoki unga teng.035 |
485 dan katta yoki teng |
275 dan katta yoki teng |
|
|
ASTM A179 |
A179 |
0.06-0.18 |
- |
0.27-0.63 |
0 dan kichik yoki unga teng.035 |
0 dan kichik yoki unga teng.035 |
325 dan katta yoki unga teng |
180 dan katta yoki teng |
|
ASTM A192 |
A192 |
0.06-0.18 |
0 dan kichik yoki unga teng.25 |
0.27-0.63 |
0 dan kichik yoki unga teng.035 |
0 dan kichik yoki unga teng.035 |
325 dan katta yoki unga teng |
180 dan katta yoki teng |
|
API 5L PSL1 |
A |
0.22 |
- |
0.90 |
0.030 |
0.030 |
331 dan katta yoki unga teng |
207 dan katta yoki unga teng |
|
B |
0.28 |
- |
1.20 |
0.030 |
0.030 |
414 dan katta yoki unga teng |
241 dan katta yoki teng |
|
|
X42 |
0.28 |
- |
1.30 |
0.030 |
0.030 |
414 dan katta yoki unga teng |
290 dan katta yoki teng |
|
|
X46 |
0.28 |
- |
1.40 |
0.030 |
0.030 |
434 dan katta yoki unga teng |
317 dan katta yoki teng |
|
|
X52 |
0.28 |
- |
1.40 |
0.030 |
0.030 |
455 dan katta yoki unga teng |
359 dan katta yoki unga teng |
|
|
X56 |
0.28 |
- |
1.40 |
0.030 |
0.030 |
490 dan katta yoki unga teng |
386 dan katta yoki teng |
|
|
X60 |
0.28 |
- |
1.40 |
0.030 |
0.030 |
517 dan katta yoki unga teng |
448 dan katta yoki unga teng |
|
|
X65 |
0.28 |
- |
1.40 |
0.030 |
0.030 |
531 dan katta yoki unga teng |
448 dan katta yoki unga teng |
|
|
X70 |
0.28 |
- |
1.40 |
0.030 |
0.030 |
565 dan katta yoki unga teng |
483 dan katta yoki teng |
|
Uglerodli choksiz po'lat quvur standarti
|
GB standarti |
Strukturaviy maqsadlar uchun choksiz po'lat quvur |
GB/T8162-2008 |
|
Suyuqlik xizmati uchun choksiz po'lat quvur |
GB/TB8163-2008 |
|
|
Past va o'rta qozon uchun choksiz po'lat quvurlar |
GB/3087-1999 |
|
|
Yuqori bosimli qozon uchun choksiz po'lat quvurlar |
GB/5310-1995 |
|
|
Choksiz karbonli po'latdan yasalgan dengiz quvurlari |
GB/T5312-1999 |
|
|
Kimyoviy o'g'it uskunalari uchun yuqori bosimli choksiz po'lat quvurlar |
GB/6479-2000 |
|
|
ASTM standarti |
Qora va issiq sink bilan qoplangan po'lat quvurlar payvandlangan va choksiz |
ASTM A53 |
|
Yuqori haroratli xizmat ko'rsatish uchun choksiz karbonli po'lat |
ASTM A106 |
|
|
Choksiz sovuq chizilgan past karbonli po'latdan issiqlik almashtirgich va kondensator quvurlari |
ASTM A179 |
|
|
Yuqori bosim uchun choksiz karbonli po'lat qozon quvurlari |
ASTM A192 |
|
|
Choksiz O'rta uglerodli qozon va o'ta isitish quvurlari |
ASTM A210 |
|
|
Mexanik quvurlar uchun choksiz uglerod |
ASTM A519 |
|
|
API standarti |
Korpus uchun choksiz po'lat quvur |
API Spec 5CT |
|
Chiziq trubkasi uchun choksiz po'lat quvur |
API Spec 5L |
|
|
DIN standarti |
Yuqori harorat uchun choksiz po'lat quvur |
DIN 17175 |
|
Sovuq chizilgan choksiz oldindan ko'rish quvuri |
DN2391 |
|
|
Choksiz dumaloq qotishmagan po'lat quvurlar maxsus talablarga javob beradi |
DIN 1629 |
Uglerodli choksiz po'lat quvurlarning tolerantliklari
|
Quvur turlari |
Quvur o'lchamlari (mm) |
Tolerantliklar |
|
Issiq haddelenmiş |
OD<50 |
±0.50mm |
|
OD 50 dan katta yoki unga teng |
±1% |
|
|
WT<4 |
±12.5% |
|
|
WT 4-20 |
+15%, -12.5% |
|
|
WT>20 |
±12.5% |
|
|
Sovuq chizilgan |
OD 6-10 |
±0.20mm |
|
OD 10-30 |
±0.40mm |
|
|
OD 30-50 |
±0.45 |
|
|
OD>50 |
±1% |
|
|
WT 1 dan kichik yoki teng |
±0,15 mm |
|
|
WT 1-3 |
+15%, -10% |
|
|
WT >3 |
+12.5%, -10% |
Afzallik
API 5L / A106 / A53 choksiz po'lat quvur ingotning quyma tuzilishini yo'q qilishi, po'latning donini tozalash va mikro tuzilmaning kamchiliklarini bartaraf etishi mumkin, shuning uchun po'lat strukturasi zich va mexanik xususiyatlar yaxshilanadi. Bu yaxshilanish asosan prokat yo'nalishida aks etadi, shuning uchun po'lat endi ma'lum darajada izotropik emas; To'kish paytida hosil bo'lgan pufakchalar, yoriqlar va bo'shashmaslik ham yuqori harorat va bosim ostida payvandlanishi mumkin.
Kamchilik
- API 5L/A106/A53 choksiz po'lat quvur Issiq prokatdan so'ng po'lat ichidagi metall bo'lmagan qo'shimchalar (asosan sulfidlar va oksidlar, shuningdek silikatlar) varaqlarga bosiladi va laminatsiya (sendvich) fenomeni paydo bo'ladi. Delaminatsiya po'latning qalinlik yo'nalishi bo'yicha cho'zilish xususiyatlarini sezilarli darajada yomonlashtiradi va payvand choki qisqarganda qatlamlararo yirtilishga olib kelishi mumkin. Payvand chokining qisqarishi natijasida kelib chiqadigan mahalliy kuchlanish ko'pincha oqish nuqtasida deformatsiyadan bir necha baravar ko'p bo'ladi, bu yukdan kelib chiqqan kuchlanishdan ancha katta.
- Noto'g'ri sovutish tufayli qoldiq stress. Qoldiq stress - bu tashqi kuch bo'lmaganda ichki o'z-o'zini muvozanat stressi. Har xil bo'laklarning issiq haddelenmiş po'latlari bunday qoldiq stressga ega. Umumiy po'latning kesim o'lchami qanchalik katta bo'lsa, qoldiq stress shunchalik katta bo'ladi. Qoldiq kuchlanish o'z-o'zidan muvozanat bo'lsa-da, u hali ham tashqi kuchlar ostida po'lat elementlarning ishlashiga ma'lum ta'sir ko'rsatadi. Deformatsiya, barqarorlik, charchoqqa qarshi va boshqa jihatlar kabi salbiy ta'sir ko'rsatishi mumkin.
- Issiq haddelenmiş po'latdan yasalgan mahsulotlar qalinligi va yon kengligi bo'yicha yaxshi nazorat qilinmaydi. Biz termal kengayish va sovuq qisqarish bilan tanishmiz, chunki issiq prokatning boshida uzunlik va qalinligi standart bo'lsa ham, sovutgandan keyin ma'lum bir salbiy farq bo'ladi va salbiy farq chekka kengligi qanchalik keng bo'lsa, qalinroq bo'ladi. qalinligi, ishlash qanchalik aniq. Shuning uchun, katta po'lat uchun, po'latning yon kengligi, qalinligi, uzunligi, burchagi va chekka chizig'i juda aniq bo'lishi kerak emas.